MEC-1037A

Ni-Al 95/5

Excellent bond coat under ceramic and metal coatings. Resists temperature to the order of 1500°F. Minimum oxide inclusions and moderate corrosion resistance. Used also for thick over lays. Good for rebuilding of worn out parts. Machinable and grindable.

MEC-1087A

Ni-Al-Mo

Good bond strength. Mild to moderate wear resistance. Harder than MEC-1037A due to the present of small quantity of molybdenum. Good for general repair of carbon steel and alloy steel components. Machinable with good finish.

MEC-1017A

Ni-Cr

This is an excellent bond coat under ceramics gives dense, clean and bright coating which resists oxidation and corrosive gases. Good for hot atmosphere to 1800°F.

MEC-1047A

Ni-Cr-Al

Good heat and oxidation resistance under corrosive gases. Also used normally as bond coat material for thermal barrier coatings. Specially used for rebuilding of Ni and Ni-alloyed components. Thermal stability upto 1800°F.

MEC-1044A

Ni-Al-Cr-Fe-Mo

Self bonding material. Good wear and oxidation resistance upto 1600°F. It is machinable to good finish.

MEC-2000A

Fe-Al

One step, self bonding material thermal stability is upto 350°F. Cheaper than Ni-based bond coats. Can also be used for thicker coatings. Most suitable for rebuilding and reclamation of ferrous components.

MEC-2003A

Ni-Cr-Fe-Si-B / Ni-Al

Hard, abrasion and wear resistance coating. Thin and thick overlays are possible. Suitable for bearing areas subjected to severe friction.

MEC-2448A

Fe-Al-Mo-C 80/10/1/Low

One step bonding material. Good for salvage and build-up of carbon steel components. Hard coating with good abrasion resistance. Machinable to good finish. Cheaper than MEC-1087A.

MEC-2449A

Fe-Al-Mo-C

Same as above with more carbon. One step self bonding material. Wider hardness range achievable. Good ground finish.

MEC-1090A

Cu-Al

Aluminium bronze coating with low shrinkage and less oxides. Resists cavitations, fretting and low temperature wear on hard surfaces. Machinable to good ground finish.

MEC-2052A

Al-Si

Good corrosion resistance. Harder, denser and gives fine texture. Machinable to good ground finish.

MEC-2404A

Ni-5Al

Reclamation of mis-machined or worn out parts of low carbon steel, stainless steel, brass, aluminium alloys. Machine bedways, wear rings, press fits, bearing seats, preferably as a top coat over bond coat powder MEC-1037A.

MEC-1031C

WC-Co / Ni-Cr-Si-C
35 / 65

This is a self fluxing powder, provides a dense and essentially pore free coating resists wear due to abrasive grains hard surfaces, erosion and fretting at temperature upto 1000°F.

MEC-1032C

WC-Co / Ni-Cr-B-Fe-Si-C
80 / 20

Dense, hard and wear resistant coating. Thermal stability upto 1000°F. Smooth finish and no thickness limitation, if cooled slowly.

MEC-1032F

WC-Co / Ni-Cr-B-Fe-Si-C
80 / 20

Dense, hard and wear resistant coating. Thermal stability upto 1000°F. Smooth finish and no thickness limitations, if cooled slowly. 

MEC-1034F

WC-Co / Ni-Cr-B-Fe-Si-C
50 / 50

This is a self fluxing powder and provides coating requiring a grinding operation. Coating resists wear by abrasive grains, erosion and fretting.

MEC-1010A

Al₂O₃ 98%

Hard, wear and corrosion resistant coating. Resists heat from molten metal and wear by natural abrasives.

MEC-1011A

Al₂O₃ - TiO₂  97 / 3

Same as above but more dense coating with good finish.

MEC-1051A

Al₂O₃ - TiO₂  87 / 13

A composite coating that is dense, hard and resists wear due to abrasion, fretting, cavitations and particle erosion.

MEC-1070A

Al₂O₃ - TiO₂  60 / 40 

Good resistance to low temperature wear due to abrasion, fretting erosion. Grinds to low RMS. Resists wetting by liquids.

MEC-2410A

Ni-Al-Al₂O₃

Better bonding on metallic substrates. Excellent wear and corrosion resistance.

MEC-1025HP

Cr₂O₃ 

Hard & wear resistant coating, Buffing and polishing fixtures,  pump seals, plungers, wear rings, diesel engine cylinder liners, exhaust, textile components, anilox rolls etc.

MEC-1230A

Ni-Fe-Si-B
94.2 / 1 / 3.2 / 1.6

Produces dense coating with hardness range from 26 - 32 Rc.

MEC-1240A

Ni-Cr-Fe-Si-B
83.4 / 9 / 3 / 3 / 1.6

Produces dense coating, essentially pore free. Highly wear and corrosion resistant. Less susceptible to cracking on hardenable steels also. Good ground finish. Hardness range from 33 - 40.

MEC-1250A

Ni-Cr-Fe-Si-B
78.4 / 121.5 / 3.0 / 3.7 / 2.4

Produce dense, essentially pore free. Highly wear and corrosion resistant. Less susceptible to cracking on hardenable steels also. Good ground finish. Hardness ranges from 45 - 50 Rc.

MEC-1260A

Ni-Cr-Fe-Si-B
73.9 / 14.5 / 4.3 / 4.3 / 3

Produces hard, dense and pore free coating that resists corrosion and wear by abrasive grains, hard surfaces, cavitations and erosion in both high and low temperatures. Fine as sprayed finish and excellent ground finish. Hardness range from 55 - 62 Rc. 

MEC-1263A

Ni-Cr-Fe-Si-B-Cu-Mo
66.3 / 14.5 / 4.3 / 4.3 / 3.1 / 12.5 / 2.5

Produces hard, dense and pore-free coating that resists corrosion and wear abrasive grains, hard surfaces, cavitations and erosion in both high and low temperatures. Fin as sprayed finish and excellent grinding finish. Hardness range from 58 - 63 Rc.